Jig for use in apparatus for securing an elongated metal member to a flat metal sheet

ABSTRACT

A method of securing metallic tubing and the like to a flat metal sheet while maintaining the flatness of the sheet so that the composite tube and sheet may be used as radiant heating or cooling panels in building interiors where distortion or wrinkling of the flat sheet would be undesirable. The apparatus comprises a heating station where a composite of sheet, of suitably disposed bonding material, and a piece of tubing in properly assembled relationship and under pressure are heated to induce a bond between the tubing and the sheet while maintaining the sheet in flat condition. An assembly station is provided including a jig in which the piece of tubing may be accurately located, means for accurately locating the jig with respect to the sheet, and means for raising and lowering the jig and for releasing the jig from the raising and lowering means so that it may move with the assembly from the assembly stations to the heating station. After the heating cycle, the assembly moves to a cooling station (which may be the same as the assembly station) for a cooling cycle. A combined assembly and cooling station may be provided on each side of the heating station, each assembly station having a jig whereby production may be speeded up.

United States Patent 1 Beck, Jr.

[4 1 Dec. 4, 1973 JIG FOR USE IN APPARATUS FOR SECURING AN ELONGATED METAL MEMBER TO A FLAT METAL SHEET [76] Inventor: Edward G. Beck, Jr., 532 S. Ft.

Thomas Ave., Ft. Thomas, Tenn.

[22] Filed: Mar. 24, 1972 [21] Appl. No.: 237,989

Related US. Application Data [60] Division of Ser. No. 673,138, Oct. 5, 1967, Pat. No. 3,514,834, which is a continuation-in-pazt of Ser. No. 523,619, Jan. 28, 1966, abandoned.

[52] US. Cl. 269/46, 269/287, 29/200 J,

29/202 R, 228/44 [51] Int. Cl B23q 1/00 [58] Field of Search 269/46, 264-267,

269/270, 275, 287; 29/157.3 C, 200 J, 200 P, 202 R, 33 G; 228/3, 4, 44, 49; 100/211, 295,

Primary Examiner-Harold D. Whitehead Assistant ExaminerHarold P. Smith, Jr. Att0meyJohn W. Melville et al.

[57] ABSTRACT A method of securing metallic tubing and the like to a flat metal sheet while maintaining the flatness of the sheet so that the composite tube and sheet may be used as radiant heating or cooling panels in building interiors where distortion or wrinkling of the flat sheet would be undesirable. The apparatus comprises a heating station where a composite of sheet, of suitably disposed bonding material, and a piece of tubing in properly assembled relationship and under pressure are heated to induce a bond between the tubing and the sheet while maintaining the sheet in flat condition. An assembly station is provided including a jig in which the piece of tubing may be accurately located, means for accurately locating the jig with respect to the sheet, and means for raising and lowering the jig and for releasing the jig from the raising and lowering [56] References Cited means so that it may move with the assembly from the assembly stations to the heating station. After the UNITED STATES PATENTS heating cycle, the assembly moves to a cooling station 2,986,811 6/1961 Rudd 228/44 may be the 53111 as the tation) for a a v cooling cycle. A combined assembly and cooling sta- C By tion may be provided on each side of the heating sta- 2,416,058 2/ 1947 Mangnall 1 0/295 X tion, each assembly Station having a j g whereby p duction may be speeded up.

. Cl 9 Draw 1 res PATENTEU 4 5 SHEET 1, BF

FIG. 1

FIG.3

I I 1 I 1 v I 1 1 l PATENTED 3.776.538

SHEU 2 OF 2 FIG. 6

FIG. 7

FIG. 9 I 72 l JIG FOR USE IN APPARATUS FOR SECURING AN ELONGATED METAL MEMBER TO A FLAT METAL SHEET CROSS REFERENCE TO RELATED APPLICATION This is a division of application Ser. No. 673,138 filed Oct. 5, 1967, now U.S. Pat. No. 3,514,834 which in turn is a continuation-in-part of copending application Ser. No. 523,619 filed Jan. 28, 1966, and now abandistort at the temperatures encountered at the respective stations. A thin metallic belt of good heat conductivity is disposed to pass over the said three blocks and means are provided to reciprocate said belt backward and forward. At each of the assembly stations means are providedfor raising and lowering a jig which is detachably secured to the raising and lowering means. The jig comprises a fiat plate of a material which will not distort at the temperatures to which it will be subdomed in the name of Edward Beck and bearing 10 jected, and has secured to its underside a block of nonthe same title as the present application.

BACKGROUND OF THE INVENTION The invention relates to the field of radiant heating and cooling panels. In such panels one face of the panel is exposed in the room or other space which is to be heated or cooled. The unexposed face of the panel is provided with tubing through which a heating or a cooling medium may be circulated to heat or cool the panel by which the room is then either cooled or heated by radiation to or from the panel. The invention more specifically relates to an apparatus for producing such composite panels and to a method of achieving a good bond in good heat exchangerelationshipbetween the panel and the tubing without destroying the flatness of the sheet. Prior attempts to bond a tubing to a flat metal shee for the above described purpose have not been satisfactory. In some cases the heat exchange relationship between the tubing and the. plate was not good and in other cases where a good heat exchange relationship was achieved, the panel was distorted so that the configuration of the tubing on the rear face of the panel could be seen on the exposed face of the panel. The appearance of the panel has not been of critical importance in situations where such panels have been used because primarily they have been used in refrigeration evaporators and the like where appearance is not a primary consideration. However, where the radiant panel is to be a wall panelor a ceiling panel in a room in a building, no ripples or undulations in the face of the panel should be apparent even when it is viewed from a very flat angle.

SUMMARY strip of a bonding material in the region where bond is desired, said bonding material having a lower melting point than the sheet and the tube, then accurately locating the tube in contact with the bonding material, clamping the sheet, over the area which is not occupied by the tube, under a uniform pressure, maintaining the assembled parts accurately ini'position while heating the assembly of the sheet,-bonding material, and tubing to a temperature above the melting point of the bonding material but below the melting point of the sheet and the tubing, and then cooling the'assembly at a relatively high temperature but below the hardening point of the bonding material until the bond has been achieved.

From the apparatus standpoint, there is provided preferably a central heating station and on each side thereof and in alignment therewith a combined assembly and cooling station. At each of said stations there is provided a flat block of metal having a flat upper surface, and the surfaces of the blocks are'in the same horizontal plane. The blocks are of a metal which will not The invention contemplates providing on the sheet a bonding material...

metallic material having relatively poor heat conductivity, but sufficient mechanical strength to retain its physical integrity without distortion at the temperatures which will be encountered. The jig will have at least the same dimensions in the horizontal plane as the sheet to which the tubing will be assembled. The underside of the non-metallic block will have one or more grooves of a width sufficient to accommodate the tubing or other member which is to be secured to the sheet, and these grooves will be of a depth greater than the thickness of .the member to be secured to the sheet. Within the groove or grooves resilient means are provided which will exert pressure against the member in the groove to urge it against the sheet' when the jig is positioned on the sheet.

The bonding material may be a solder either in the form of a ribbon or wires, or in the form of a metallic powder which may be applied to the sheet very accurately by screen printing. The bonding material may also be one of the thermosetting resin adhesives. Means are provided in connection with the jig to insure accurate location of the tubing in the jig so that the tubing will be assembled in accurate relationship to the bonding material disposed on the sheet. Thus,-when the jig is lowered into contact with the sheet and disconnected from the lowering device, the belt moves the assembly to the heating station to create the bond, and thereafter the belt moves the assembly to the cooling station which may be at the same point as the assembly station and may, therefore, be provided with .means for heating to a temperaturebelow the hardening point of the BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a somewhat diagrammatic view in elevation of an apparatus according to the present invention.

FIG. 2 is a fragmentary plan view of one of the assembly stations.

FIG. 3 is a bottom view of the jig. 7

FIG. 4 is-a fragmentary cross sectional view taken on the line 4- -4 of FIG. 3 but invertedso as to be right sideup.

FIG. 5 is a fragmentary elevational view as seen from the right of FIG. 3.

FIG. 6 is a cross sectional view through the assembly of jig, tub ng, and sheet as disposed on the belt at the assembly stations as seen on the line 6-6 of FIG. 3.

DESCRIPTION OF THE PREFERRED EMBODIMENTS In FIG. 1 the heating station is indicated at B and assembly and cooling stations are indicated at A and C. At each station there is provided a flat block of uniform thickness with flat top and bottom surfaces, as at 10, 1 1 and 12. These blocks are of a material which will not have its flatness distorted at temperatures encountered during the operations which will be conducted. While these plates may be an annealed steel, they are preferably made of cast aluminum tooling plate such as manufactured and sold by Aluminum Corporation of America as No. 300 Cast Aluminum Tooling Plate. It will be seen that the upper surfaces of plates 10, 11 and 12 are in a common plane and a belt 13 is arranged to pass over them. The belt 13 must have good heat conductivity and may be of perforated aluminum having a thickness of 0.032 inches. In FIG. 1 an assembly 14b is shown at the heating station in broken lines, while another assembly is being assembled at assembly and cooling station A. At 14c there is shown another assembly which has cooled down and is about to be removed from the assembly and cooling station C.

In order to insure that the tubing or other element to be joined to the sheet is located on the sheet in its proper location, and that the sheet is confined by a uniform pressure over substantially its entire surface, a jig 14 is provided as best seen in FIGS. 3 to 6 inclusive. This jig comprises a plate 17 which is also preferably a cast aluminum tooling plate as described above, and may have a thickness, for example, of one inch. Secured to the plate 17 by means of bolts 18 is a block 19 of a non-metallic material which has relatively poor heat conductivity but sufficient mechanical strength to retain its physical integrity without distortion at soldering, brazing or polymerizing temperatures. By way of example, the block 19 may be made from asbestos fiber and an inorganic binder such as is available from Johns- Manville Corporation under the registered trademard MARANITE. This material has a density of 65 pounds per cubic foot and by way of example the block 19 may have a thickness of 1 inch.

The underside of the block 19 is provided with th groove or grooves 20. In the particular embodiment shown, the groove is sinuous or S-shaped such that a previously bent piece of tubing may lie in the groove 20. The width of the groove 20 is such as to accommodate comfortably the tubing 15 and its depth is greater than the diameter of the tubing 15. Within the groove 20 means are provided to urge the tubing against the sheet when the jig is laid on the sheet and these means may be a strip 21 of a resilient material which will maintain its resilience at the temperatures encountered as, for example, a silicone rubber compound of 30 durometers. It will be understood that the thickness of the strip 21 is greater than the difierence between the diameter of the tube 15 and the depth of the groove 20. Instead of the strip 21, stainless steel spring members may be used. The springs will of course be made of an appropriate alloy which will retain its spring properties at the operating temperatures of the process. They perform the same function as the resilient strip 21.

The tubing 15 is accurately located and held in the jig by means of pressure pins 60. The pins 60 slide in holes in blocks 63 secured to the plate 17 and may be actuated in any desired manner as, for example, by air cylinders, to advance the pins into contact with the tubing, and when air pressure is released the springs 61 will serve to retract the pins 60 out of the way. Preferably the pins engage the tubing centrally of the convex loops as shown in FIG. 3.

Since FIG. 3 is a bottom view and the jig is actually disposed as seen in FIG. 1, additional means may be provided to prevent the tubing 15 from falling out of the jig. This is accomplished as shown in FIG. 5 by means of the sliding retainers 64. These are simply plates secured to the block 17 by means of bolts 65 passing through a slot 66 so that the plate 64 may be slid back and forth. They are provided with a finger 64a which engages under the ends of the tubing 15 where they emerge from the groove 20. i

Each of the jigs 14 is rigidly connected to a shank 34 which is slidable in a guide tube 35 fixedly mounted to a frame member or the like 350. Means (not shown) are provided to raise and lower the jig 14 and its shank 34 with respect to the guide tube 35; and when the jig l4'has been lowered onto the sheet 16, the jig 14 may be disconnected from the shank 34. It will be observed that the shank 34 fits snugly into a collar 80 rigidly se cured to the jig 14, and is releasably secured thereto by a pin 81. The shank fits snugly in the guide tube 35, and is provided with a longitudinal groove 82 which is engaged by a key 83 fastened in the guide tube 35, to prevent rotation of the jig when it is raised. Thus when the pin 81 is withdrawn, the shank 34 may be raised without the jig 14, which remains on the sheet as shown at station B. Y

The bonding material may be applied to the sheet before the sheet is placed on the assembly block in a number of ways depending upon the material of the bonding agent. If the'bonding agent is a ribbon of solder, use may be made of a template 66 as shown in FIG. 7. The template 66 will be provided with slots 67 and this template 66 is exactly the same size as the sheet. Thus, when the template is laid on the sheet with its edges coinciding therewith, the strips of solder may be laid in the slots 67. The slots will be slightly wider and slightly longer than the strip so thatthe strip of solder will be easily accommodated therein. The solder strips may be coated with a flux which is quite viscous and sticky at room temperature but becomes relatively fluid when it is heated. Therefore, the flux may be heated before it is applied to both sides of the solder strips 22. Now when these flux coated strips are laid on the sheet 16 in the space provided in the template 66, they quickly cool so that the flux again becomes viscous and sticky and effectively adheres the solder strips to the sheet 16 so that they will not move out of position when the sheet is picked up and moved to the assembly station.

If the configuration of the panel is such that the strips of solder 22 are quite long, difi'lculty will be encounteredbecause of the fact that solder in ribbon form is usuallycharacterized by camber sothat it is difficult to locate it in the slot 67. Therefore, a preferred way of applying solder is by screen printing. In FIGS. 8 and 9 there is shown a screen comprising a thin sheet of metal 70 having the same width and length as the sheet 16. Slots 72 are provided through which the bonding agent is to pass and a layer of wire mesh 71 is bonded to the sheet 70. This screen is placed on the sheet 16 with the edges coinciding and a paste of solder and flux is forced through the mesh of the screen 71 where the slots 72 permit it and thus films of solder-flux paste are deposited on the sheet in proper position. lt will be understood that other bonding agents which are initially in paste form may be applied to the sheet by screen print-' It will now be clear that having applied the bonding material to the sheet 16 in a predetermined accurate position and knowing that the tubing will be accurately positioned by means of the jig 14, it is only necessary to insure that the sheet with the bonding material applied thereto will be accurately positioned at the assembly station.

The sheets which are ultimately formed into panels by a flanging operation will have the cut out corners or notches 36. For the purpose of positioning the sheet at the assembly station, locater arms 30 are provided which are secured to members 31 so that they may be adjusted, and the members 31 intum are rotatable with the shaft 32 which is mounted in the base 33. With the locater fingers 30 in the position shown at Station A in FlG. l, the sheet 16 is pushed against the fingers which engage in the notches 36. The fingers 30 are then rotated out of the way so that the jig 14 may be lowered. Thus, it is now assured tha when the jig 14 is lowered onto the sheet bearing the bonding material 22, the tubing will be precisely located with respect to the sheet and the strips of bonding material.

As a solder there may be used a composition of 91 per cent tin and 9 per cent zinc with a flux available from Aluminum Corporation of America under the name ALCOA NO. 62. This solder may be positioned in strip or ribbon form or in the form of wire. As pointed out above, a powdered solder-flux combination may also be used. It is to be understood that the word strip as used in the claims is intended to cover a bonding material regardless of its nature-or its specific physical form. If solder is used in the form of a ribbon, the tubing 15 lies upon the ribbon. It is is in the form of wire, the wire is laid in such manner that the tubing engages wire on one or both sides of the tubing.

In the particular example illustrated, the flat sheet member is of a thickness of 0,040 inches and is of aluminum. The tubing is of copper, having a half inchinside diameter and a wall thickness of 0.028 inches. The weight of the jig is sufficient to apply to the sheet- 16 an average unit pressure of approximately 014 psi. The heating station is heated'by any desired means so that the block 11 will attain a temperature of about 510 F. This temperature is above the melting point of the bonding material but below the melting point of the sheet and the tubing and of course the belt. It may be desirable at the heating station to increase the unit pressure to about 0.65 psi by placing additional weight on top of the jig. With the type of solder described, the assembly is held at Station B for approximately 3 minutes. The bonding agent will form fillets between the tubing and sheet on both sides of the tubing as clearly seen in FIG. 6. If the solder is in wire form, the tubing is of course pressed against the sheet rather than on top of the ribbon and when the solder melts it flows in and forms fillets on both sides of the tubing'in the same way. Good wetting can be obtained and the assembly will be ready for cooling afterabout three minutes.

it is critically important to control the temperature at which the bonding material is cooled in order to avoid wrinkling or distortion of the sheet 16. There is'a maximum difference in temperature between the heating block 11 and the cooling blocks 10' and 12 beyond which distortion or wrinkling of the sheet 16 will probably be experienced. This maximum difference must be determined for each combination of sheet material and thickness, and tubing material and size. Actually, therefore, the stations A and C are also heating stations in that the blocks 10 and 12 are heated. For the particular conditions herein described, they are heated to a temperature of about 300 F. With the particular solder and materials described herein, the solder will solidify in approximately two minutes with blocks 10 and 12 at stations A or C at a temperature of about 300 F. At this time, the solder will have developed sufficient physical properties that the assembly 14C may be removed from the machine. Before removal, of course, the members 64 will be withdrawn.

It will be noted that from the time the jig is assembled over the sheet, the sheet 16 is tightly confined over its entire area except for the grooves 20, between the bottom face of the non-metallic block 19 and the top face of the belt 13, which in turn is supported on the top faces of blocks 10, 11 and 12 successively. The tube 15 is maintained tightly in' contact with the sheet 16 by the springs or the resilient strips 21.

The arrangement of FIG. 1 is advantageous because of the time factors involved. Thus, while one assembly is at the heating station B, a previously heated assembly may be at the cooling station at C, while another assembly is being prepared at station A. When the belt 13 moves to the right, that assembly which has been heated at B will be moved to C for cooling and since the cooling cycle takes only about 2 minutes, a new assem bly can then be placed at C so that when the belt moves back toward the left, the new assembly will move to the heating station B while the just heated assembly will move to the cooling station at A. Obviously, this greatly increases the productive capacity of the machine.

The practice of the invention as herein described will produce an excellent joint bond from the mechanical standpoint and from the heat transfer standpoint, and

the aluminum sheet will retain its high degree of flatness without distortion. If there should be a departure from flatness as the assembly cools down to room temperature due to the difl'erence in thermal coefficient of expansion between sheet and tube, such departure from flatness will take the form of a long radius unifonn chamber inone direction which can be removed later by 'a simple straightening operation so as to leave the sheet substantially fiat without wrinkles, undulations or other evidence of localized distortion.

It will be understood that while the invention has been described particularly with respect to bonding tubing to a sheet, it is also adaptable to the securing of any sort of stiffening elements of the same or different metal to one face of a sheet where it is desired to maintain the flatness of the sheet.

It will be understood that various modifications may be made and that no limitation not specifically set forth in the claims is intended or should be implied.

The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows:

1. A jig for use in joining metallic tubing to a flat sheet of metal, comprising a flat plate of a metal which will remain substantially undistorted at joining tempernon-metallic material having good mechanical strength at said joining temperatures, and having relatively poor heat conductivity and having at least the same length and width as said plate and secured to the underside of said plate, said block having on its underside a recess configured to accommodate said tubing and of a depth greater than the diameter of said tubing, and resilient means secured in said recess, said resilient means being of a material which will maintain its resilience at said joining temperatures, said resilient means exerting pressure against said tubing when said tubing is within said recess and tangent to the plane of the bottom surface of said jig.

2. A jig according to claim 1, wherein locating means are provided to insure proper positioning of said tubing in said recess, and releasable means are provided for retaining said tubing in said recess during positioning on a sheet of metal to which said tubing is to be joined.

3. A jig according to claim 2, wherein said recess is of sinuous configuration for use with tubing of congruent sinuous configuration, and wherein said locating means are in the form of pins entering said recess at convex regions of said sinuous recess, and provided with means to urge them into contact with a piece of tubing disposed in said recess.

4. A jig according to claim 1, in combination with means for raising it for insertion of a piece of tubing, and lowering it for positioning the piece of tubing on a sheet to which the tubing is to be secured, and means for releasing said jig from said raising and lowering means.

O I I =0 

1. A jig for use in joining metallic tubing to a flat sheet of metal, comprising a flat plate of a metal which will remain substantially undistorted at joining temperatures, and having a length and width at least substantially equal to those of said sheet of metal, a block of non-metallic material having good mechanical strength at said joining temperatures, and having relatively poor heat conductivity and having at least the same length and width as said plate and secured to the underside of said plate, said block having on its underside a recess configured to accommodate said tubing and of a depth greater than the diameter of said tubing, and resilient means secured in said recess, said resilient means being of a material which will maintain its resilience at said joining temperatures, said resilient means exerting pressure against said tubing when said tubing is within said recess and tangent to the plane of the bottom surface of said jig.
 2. A jig according to claim 1, wherein locating means are provided to insure proper positioning of said tubing in said recess, and releasable means are provided for retaining said tubing in said recess during positioning on a sheet of metal to which said tubing is to be joined.
 3. A jig according to claim 2, wherein said recess is of sinuous configuration for use with tubing of congruent sinuous configuration, and wherein said locating means are in the form of pins entering said recess at convex regions of said sinuous recess, and provided with means to urge them into contact with a piece of tubing disposed in saId recess.
 4. A jig according to claim 1, in combination with means for raising it for insertion of a piece of tubing, and lowering it for positioning the piece of tubing on a sheet to which the tubing is to be secured, and means for releasing said jig from said raising and lowering means. 